Paste

 

 

  • 被動元件

Pastes for Terminal Electrodes of Passive Components(Firing type)
Product Number
Characteristics
Applications
Metal
Application method
Sintering
condition
IP3600 series
High reliability; lead free
Chip inductors
Ag
Dipping method
600-700℃
PC4700 series
Excellent adhesive strength;
good solderability
Chip capacitors
Ag
Dipping method
650-750℃
VP3700 series
Excellent adhesive strength;
good solderability
Chip varistors
Ag
Dipping method
750-830℃
VP3800 series
Excellent adhesive strength;
good solderability
Chip varistors
Ag
Dipping method
750-830℃
PC3800 series
Excellent adhesive strength;
good solderability
Core
Ag
Pad printing
650-700℃
Pastes for Terminal Electrodes of Passive Components(Curing type)
Product Number
Characteristics
Applications
Metal
Application method
Sintering
condition
EP9100 series
Excellent adhesive ; Good solderability
Mini choke
Ag
Dipping or Pad Printing
180℃x60min

Pastes for Internal Electrodes of Passive Components

Product Number
Characteristics
Applications
Filler
Application method
Sintering
condition
IP3100 series
Low resistance
Chip inductors
Ag
Screen printing
850-920℃
PC2200 series
Excellent printing performance;Various shrinkage rates
Chip  varistor
80Ag-20Pd
Screen printing
1000-1080℃
PC7700 series
Excellent printing performance;Various shrinkage rates
Chip  varistor
70Ag-30Pd
Screen printing
1050-1100℃
PC2900 series
Excellent printing performance;Various shrinkage rates
PZT
95Ag-5Pd
Screen printing
900-950℃
PC2100 series
Excellent printing performance;Various shrinkage rates
Chip capacitors
90Ag-10Pd
Screen printing
950-990℃
PC2900 series
Excellent printing performance;Various shrinkage rates
Chip capacitors
95Ag-5Pd
Screen printing
900-950℃

Copper paste for MLCC

Product Number
Characteristics
Applications
Metal
Viscosity
10 rpm [Pa・s]
Curing
condition
PC6088
Adhesion
NPO
Cu
65
850℃, 60min.
PC65751
Adhesion
X7R
Cu
65
850℃, 60min.

Silver paste for Resistance

Product Number
Characteristics
Applications
Metal
Viscosity
10 rpm [Pa・s]
Curing
condition
PR22741
Low silver content
Top
Ag
220
850℃, 60min.
PR2138
Low silver content
Back
Ag
180
850℃, 60min.